無錫環(huán)氧自流平地坪施工最佳環(huán)境溫度是在10-35℃，溫度過低或過高都會對環(huán)氧地坪漆施工產(chǎn)生不良影響，無法保證施工后的效果，下面環(huán)氧地坪漆廠家就給大家分析溫度過低或者過高對環(huán)氧地坪漆施工產(chǎn)生的影響。溫度高于30度，會導(dǎo)致涂料的稠度增加、干結(jié)報廢，嚴(yán)重的話還會出現(xiàn)爆聚現(xiàn)象。溫度過高對環(huán)氧地坪漆施工的影響，導(dǎo)致工人還無法把桶內(nèi)環(huán)氧地坪漆材料施工完，環(huán)氧地坪漆就已經(jīng)沒有用了。一般我們都采用少量多次的方法配漆，或者選用沸點高、揮發(fā)慢的稀釋劑調(diào)整溫度對環(huán)氧地坪漆施工的影響。

The optimum environmental temperature for epoxy floor paint construction is 10-35 C, too low or too high temperature will have a negative impact on the construction of epoxy floor paint, can not guarantee the effect after construction. The following epoxy floor paint manufacturers will give you an analysis of the impact of too low or too high temperature on the construction of epoxy floor paint. If the temperature is higher than 30 degrees, the consistency of the coating will increase, the dry end will be scrapped, and if serious, the explosion will occur. The influence of high temperature on the construction of epoxy floor paint leads to the fact that workers can not finish the construction of floor paint materials in barrels, and floor paint is no longer useful. Generally, we use a small number of times to prepare the paint, or choose a diluent with high boiling point and slow volatilization to adjust the influence of temperature on the construction of epoxy floor paint. 

一、溫度過低對環(huán)氧地坪漆施工的影響

I. Effect of Low Temperature on Construction of Epoxy Floor Paint

1、減慢涂料反應(yīng)。

1. Slow down the reaction of paint.

雙組分的地坪漆材料(我司的為雙組分)施工，需要現(xiàn)場將甲、乙組分按一定比率混合，攪拌均勻，讓雙組分充分反應(yīng)，這樣才能保證地坪的效果。但如果溫度低于5℃，反應(yīng)將會降低或減緩，這會嚴(yán)重影響地坪涂料的固化性能。而固化性能的降低，將導(dǎo)致涂膜表面干得很慢，會增加涂膜被灰塵，雜物，或者昆蟲(蒼蠅、蚊子)污染的可能。

In the construction of two-component floor paint materials (our company's two-component), it is necessary to mix components A and B at a certain ratio on site, mix evenly, and make the two components react fully, so as to ensure the effect of the floor. However, if the temperature is lower than 5 C, the reaction will be reduced or slowed down, which will seriously affect the curing performance of floor coatings. Decreased curing performance will result in a slow drying of the film surface, which will increase the possibility that the film will be contaminated by dust, debris, or insects (flies, mosquitoes).

2、黏度成倍增長。

2. Viscosity doubles.

無溶劑的環(huán)氧自流平地坪涂料無需刮涂，靠流平性保證地坪的平整度。但低溫下，地坪涂料的黏度會成倍增加，流平性能將降低。而不靠流平性的涂料，刮涂時會因為流動、流平性能變差，而出現(xiàn)鏝刀痕的缺陷。

Solvent-free epoxy self-leveling floor coating does not need to scratch, depending on leveling to ensure the evenness of the floor. However, at low temperature, the viscosity of the floor coating will be doubled and the leveling performance will be reduced. However, without leveling coating, the defect of trowel marks will appear when scraping because of the poor flow and leveling performance.

3、降低涂膜質(zhì)量。

3. Reduce the quality of the film.

由于固化反應(yīng)減慢，或者完成不能固化，涂膜的強度、硬度、耐磨性都將會降低，而且會更容易出現(xiàn)環(huán)氧樹脂地坪脫離等問題，嚴(yán)重的影響環(huán)氧地坪漆的使用壽命。

The strength, hardness and wear resistance of the coatings will be reduced due to the slow curing reaction or the failure of curing, and the problems of epoxy resin floor detachment will occur more easily, which will seriously affect the service life of the epoxy floor paint.